Bar and Rod
Plate and Sheet
Strip
Pipe and Tube
Wire
Welding
Powder Material
Cast Products
Forged Products
Fittings
Fastening
Round Bar:
φ2–500 mm, 1–6 m length
Flat/Square Bar:
4–100 mm thickness/width
Hex Bar:
A/F 3–100 mm
Hollow Bar:
OD 20–300 mm
Sheet:
0.3–6 mm thickness
Medium Plate:
6–25 mm thickness
Heavy Plate:
25–100 mm thickness
Standard Strip:
0.05–3 mm thick,
10–600 mm wide
Precision strip:
0.01–0.5 mm thick,
tight tolerance ±0.005 mm
Foil:
0.005–0.1 mm thick
Seamless Tube:
OD 6–450 mm,
WT 1–50 mm,
1–12 m length
Welded Tube:
OD 10–600 mm,
WT 1–20 mm
Capillary Tube:
OD 1–10 mm,
WT 0.1–2 mm
Wire Form:
Cold Drawn Wire,
Bright Wire,
Spring Wire,
Fine Wire,
Ultra-fine Wire
General Diameter:
φ0.1–10 mm
Coil Weight:
50–500 kg,
customizable tolerance
Solid Wire:
φ0.8–4.0 mm
Flux-cored Wire:
φ1.2–4.0 mm
Welding Rod:
φ2.0–5.0 mm
Powder Form:
AM 3D Printing Powder,
Spherical Powder,
Gas-atomized Powder,
Water-atomized Powder
Particle Size:
10–150 μm
Sphericity:
≥90% for AM grade
Cast Ingot:
φ200–800 mm
Precision Casting:
min wall 0.5 mm
Cast Pipe:
OD 100–600 mm,
WT 10–50 mm
Forged Bar:
Φ35–500 mm
Forged Ring:
OD 200–2000 mm
Forging Weight:
1–5000 kg
Fittings Form:
Elbow, Tee, Reducer, Flange, Cap, Outlet, Lap Joint
Size range:
1/2''–24'' (DN15–DN600)
Wall thickness:
Sch10–Sch160, STD, XS, XXS
Pressure Class:
150–2500 LB
Fastening Form:
Bolt, Nut, Screw, Stud, Washer, Pin, Rivet
Metric: M3–M64
Imperial: #4–2.5''
Length: 6–500 mm
N09945 is an age-hardenable, high-strength, corrosion-resistant nickel-iron-chromium alloy with additions of molybdenum, copper, niobium, titanium and aluminium. This datasheet presents the material within the American (ASTM / ASME / UNS) standard system.
Developed for demanding oil-and-gas service, N09945 pairs very high strength with excellent corrosion resistance. Its nickel content resists chloride-induced stress-corrosion cracking; nickel with molybdenum and copper gives outstanding resistance to reducing media; molybdenum and niobium add resistance to pitting and crevice corrosion; and chromium provides resistance in oxidizing environments. Niobium, titanium and aluminium drive the age-hardening reaction, forming γ′ (Ni₃(Ti,Nb,Al)) and γ″ (Ni₃Nb) precipitates that give the alloy a higher strength than the single-γ′ alloy 925. With resistance to sulfide stress cracking in hydrogen-sulfide environments, it is qualified under NACE MR0175 / ISO 15156-3 and is supplied in the solution-annealed and aged condition.
Typical applications include down-hole and surface well equipment — tubular products, valves, hangers, landing nipples, tool joints and packers — and high-strength fasteners and shafting for sour, high-pressure / high-temperature wells.
| Property | Value | Unit |
|---|---|---|
| Density | 8.20 | g/cm³ |
| Melting range | 1300–1370 | °C |
| Elastic modulus | 203 | GPa |
| Coefficient of thermal expansion (20–100 °C) | 13.0 | µm/m·°C |
| Thermal conductivity (20 °C) | 11.0 | W/m·K |
| Specific heat (20 °C) | 435 | J/kg·K |
| Structure | Austenitic (FCC) | — |
| Element | Symbol | Min % | Max % | Role in Alloy |
|---|---|---|---|---|
| Nickel | Ni | 45.0 | 55.0 | Austenite former; chloride-SCC resistance; γ′ matrix |
| Iron | Fe | Balance | — | Base element |
| Chromium | Cr | 19.5 | 23.0 | Oxidation / pitting resistance |
| Molybdenum | Mo | 3.00 | 4.00 | Pitting / crevice / reducing-acid resistance |
| Niobium | Nb (+Ta) | 2.50 | 4.00 | γ′ / γ″ (Ni₃Nb) precipitation strengthening |
| Copper | Cu | 1.50 | 3.00 | Resistance to reducing chemicals |
| Titanium | Ti | 0.50 | 2.50 | γ′ (Ni₃Ti) precipitation strengthening |
| Aluminium | Al | — | 0.70 | γ′ formation |
| Carbon | C | — | 0.03 | Residual |
Solution-annealed and aged condition, typical values for UNS N09945 (125 ksi minimum yield grade).
| Condition | Property | Value |
|---|---|---|
| Solution annealed & aged | Tensile strength (UTS) | ≥1035 MPa (150 ksi) |
| Solution annealed & aged | 0.2% yield strength | ≥862 MPa (125 ksi) |
| Solution annealed & aged | Elongation at break | ≥18 % |
| Solution annealed & aged | Reduction of area | ≥35 % |
| Solution annealed & aged | Hardness | ≤40 HRC |
Confirm against the mill test report. Higher minimum-yield grades (e.g. 140 ksi) are available; the hardness limit and microstructure are controlled for sour-service qualification.
| Environment | Performance | Notes |
|---|---|---|
| Sour gas (H₂S / CO₂) | Excellent | Qualified to NACE MR0175 / ISO 15156-3 |
| Chloride stress-corrosion cracking | Excellent | High nickel content |
| Pitting / crevice corrosion | Excellent | Molybdenum + niobium bearing |
| Reducing media | Excellent | Ni + Mo + Cu |
| Sulfide stress cracking (SSC) | Excellent | Resistant; HPHT sour-well service |
The alloy resists general corrosion, pitting, crevice corrosion, stress-corrosion cracking and sulfide stress cracking in both reducing and oxidizing environments, making it well suited to deep, sour, high-pressure / high-temperature oil-and-gas wells.
An age-hardenable corrosion-resistant alloy; strengthened by solution annealing followed by two-step ageing.
Solution Treatment Solution anneal at approximately 982–1065 °C, soak about 1.5–4 hours, and cool (air or water quench).
Precipitation Hardening (Ageing) Age at approximately 677–732 °C (1250–1350 °F) for 4–9 hours, furnace cool to about 599–643 °C (1110–1190 °F), hold for a total ageing time of at least 12 hours, then air cool or water quench — precipitating γ′ (Ni₃(Ti,Nb,Al)) and γ″ (Ni₃Nb). The schedule meets the requirements of NACE MR0175.
Good weldability; welding is performed in the solution-annealed condition with post-weld ageing. Matching or compatible nickel-alloy fillers are used.
| Welding Process | Applicability | Filler / Consumable |
|---|---|---|
| GTAW / TIG | Good | Matching or compatible nickel-alloy filler |
| GMAW / MIG | Good | Compatible filler |
| EBW / laser | Good | Autogenous or matching filler |
Weld in the solution-annealed condition; apply post-weld solution and ageing to develop properties.
Machining Guidelines
| Parameter | Recommendation |
|---|---|
| Preferred condition | Solution-annealed for machining, then age |
| Machinability | Difficult; rigid setups, carbide tooling, slow speeds |
| Coolant | Ample coolant |
Forming Processes
| Process | Notes |
|---|---|
| Cold forming | In the annealed condition; work-hardens; pump-shaft grade is cold-worked and aged |
| Hot forming | Readily forged; solution and age afterward |
| Industry | Typical Components | Key Requirements |
|---|---|---|
| Oil & gas (downhole) | Tubulars, hangers, landing nipples, packers | High strength + sour-service resistance |
| Oil & gas (surface) | Valves, tool joints, wellhead components | Strength + H₂S / CO₂ resistance |
| HPHT wells | High-pressure / high-temperature hardware | Strength + SSC / SCC resistance |
| Marine / pump | Fasteners, pump and shafting components | Strength + corrosion resistance |
| Product Form | Standard | Notes |
|---|---|---|
| Bar, rod and forging stock | ASTM B637 · API 6A | UNS N09945 |
| Tube and pipe | UNS N09945 | Sour-service product |
| Pump-shaft grade | UNS N09945 | Cold-worked and aged |
| Sour-service qualification | NACE MR0175 / ISO 15156-3 | Up to NACE level VII |
Age-hardenable nickel-iron-chromium alloy with Mo, Cu, Nb, Ti and Al. UNS N09945.
| UNS | Strengthening | Yield Strength | Best Used For |
|---|---|---|---|
| N09945 | γ′ + γ″ (Nb, Ti, Al) | 125–160 ksi | High-strength sour-service Ni-Fe-Cr; deep HPHT oil & gas wells |
| N09946 | γ′ + γ″ (Nb, Ti, Al) | 140–160 ksi | Enhanced 945X variant for extreme HPHT |
| N09925 | γ′ (Al, Ti) | ~110 ksi | Age-hardened 825; sour service (925) |
| N07725 | γ′ + γ″ (Nb, Ti) | ~120 ksi | Age-hardened 625; sour service (725) |
| N07718 | γ′ + γ″ (Nb, Ti) | ~150 ksi | Most-used high-strength superalloy (718) |